Determining the feasibility of H2O2 production at a graphite cathode using bond dissociation energy: comparing simple and nitrogen doped cathodes
نویسنده:
سال انتشار: p2019
تعداد صفحات: 17
زبان فایل: انگلیسی
فرمت فایل: pdf
حجم فایل: 2MB
رمز فایل: www.ketabdownload.com
قیمت: 100,000ريال

افزودن به سبد دانلود

10.1007/s11164-019-03793-5

Abstract --- Hydrogen peroxide (H2O2) is commercially produced by catalytic oxidation of anthrahydroquinone, which is energy-intensive. Electrochemical production of hydrogen peroxide production through oxygen reduction reaction (ORR) is a sustainable approach, primarily due to its significance in energy conversion systems such as fuel cells. Low temperature fuel cells use graphite as a cathode for H2O2 synthesis. However, the catalytic activity of a graphite cathode for a two-electron oxygen reduction reaction must be improved. Nitrogen doping is an efficient approach to modify the electrochemically active surface of the graphite cathode. Therefore, quantum chemical approaches are essential to comprehend the molecular nature of the processes at the cathode. DFT/B3LYP/6-31G* method was employed and bond dissociation energy (BDE) analysis was performed to determine the feasibility of H2O2 production at graphite and nitrogen-doped graphite (Graphite-N) cathodes. According to the suggested mechanism, oxygen adsorption is the first step of the ORR. Calculated values showed that with energy value of 23.50 kcal/mol oxygen adsorption at the Graphite-N cathode is energetically more favorable than the graphite cathode (Ead = 65.08 kcal/mol). Considering the ORR mechanism, a second-electron oxygen reduction is identified as a key step for both H2O and H2O2 production. Therefore, BDEs were compared at the second-electron oxygen reduction step. On average, − 320.92 and − 286.04 kcal/mol of BDEs for graphite and Graphite-N cathodes showed the feasibility of H2O2 production at the Graphite-N cathode. The results are in agreement with the literature. Thus, it is concluded that nitrogen doping of the graphite cathode increases the feasibility of H2O2 production


دانلود مقاله تعیین امکان تولید H2O2 در یک کاتد گرافیت با استفاده از انرژی تفکیک پذیری پیوند , مقایسه کاتد های ساده و داپ شده با نیتروژن , دانلود مقاله , تعیین امکان تولید H2O2 در یک کاتد گرافیت , استفاده از انرژی تفکیک پذیری پیوند , مقایسه کاتد های ساده , داپ شده با نیتروژن , Determining the feasibility of H2O2 production at a graphite cathode using bond dissociation energy: comparing simple and nitrogen doped cathodes
مقالات علمی

نام و نام خانوادگی:
متن:
تصویر:

نظرات و پیشنهادات

عضویت در سایت

پشتیبانی آنلاین

نام و نام خانوادگی:
پست الکترونیک:
متن:

نام کاربری:
کلمه عبور:
کلمه عبور را بخاطر بسپار
کلمه عبور خود را فراموش کرده ام
عضویت در سایت

نام و نام خانوادگی:
پست الکترونیک:
شماره موبایل:
گفتگو با:


کتاب دانلود : دانلود کتاب های علمی و دانشگاهی روز دنیا. هرگونه کپی برداری از محتوا، قالب، و طرح های به کار رفته در این سایت شرعا و قانونا ممنوع می باشد، و پیگرد قانونی دارد.